Influences of deposition and crystallization kinetics on the properties of silicon films deposited by low-pressure chemical vapour deposition from silane and disilane - LAAS - Laboratoire d'Analyse et d'Architecture des Systèmes Accéder directement au contenu
Article Dans Une Revue Thin Solid Films Année : 2010

Influences of deposition and crystallization kinetics on the properties of silicon films deposited by low-pressure chemical vapour deposition from silane and disilane

Résumé

The paper deals with the properties of silicon films obtained by low-pressure chemical vapour deposition (LPCVD). Two gaseous sources characterized by different deposition temperatures, i.e. disilane Si2H6 (420 – 520°C) and silane SiH4 (520 – 750°C), were studied in order to understand the influences of the deposition and crystallization kinetics on the silicon films properties. Thus, the deposition of amorphous, semi-crystallized and polycrystalline silicon films was related to the "volume random" and "surface columnar" crystallization phenomena, highlighting a linear relationship between the refractive index and the polysilicon volume fraction and, showing complex residual stress dependency with process conditions. Finally, by introducing the ratio Vd/Vc between the deposition and crystallization rates as a major parameter, different deposition behaviours and related semi-empirical relationships were defined in order to characterize fully the various properties of LPCVD silicon films (microstructure, polysilicon volume fraction, refractive index and residual stress) according to the chosen gaseous source, silane or disilane.
Fichier principal
Vignette du fichier
manuscript_vf.pdf (815.8 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-01511365 , version 1 (20-04-2017)
hal-01511365 , version 2 (14-04-2018)

Identifiants

Citer

Pierre Temple-Boyer, Bernard Rousset, Emmanuel Scheid. Influences of deposition and crystallization kinetics on the properties of silicon films deposited by low-pressure chemical vapour deposition from silane and disilane. Thin Solid Films, 2010, 518 (23), pp.6897-6903. ⟨10.1016/j.tsf.2010.07.037⟩. ⟨hal-01511365v2⟩
146 Consultations
87 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More